%0 Journal Article
%T SOLIDIFICATION CHARACTERISTIC OF TITANIUM CARBIDE PARTICULATE REINFORCED ALUMINIUM ALLOY MATRIX COMPOSITES
%A N. FATCHURROHMAN
%A S. SULAIMAN
%A M.K.A. ARIFFIN
%A B.T.H.T BAHARUDDIN
%J Journal of Engineering Science and Technology
%D 2012
%I Taylor's University
%X In this research solidification characteristic of metal matrix composites consisted of titanium carbide particulate reinforced aluminium-11.8% silicon alloy matrix is performed. Vortex mixing and permanent casting method are used as the manufacturing method to produce the specimens. Temperature measurements during the casting process are captured and solidification graphs are plotted to represent the solidification characteristic. The results show, as volume fraction of particulate reinforcement is increased, solidification time is faster. Particulate reinforcement promotes rapid solidification which will support finer grain size of the casting specimen. Hardness test is performed and confirmed that hardness number increased as more particulate are added to the system.
%K Metal matrix composites
%K Aluminium alloy
%K Titanium carbide particulate
%K Solidification characteristic
%U http://jestec.taylors.edu.my/Vol%207%20Issue%202%20April%2012/Vol_7_2_248_256_N.%20FATCHURROHMAN.pdf