%0 Journal Article
%T Caracterizaci¨®n nanomec¨¢nica de la estructura celular y anat¨®mica de Eucalyptus nitens y su relaci¨®n con la frecuencia de grietas y rajaduras en madera redonda Characterization nanomechanics of wood cell structure and anatomy in Eucalyptus nitens and its relation to the cracking and fractures in round wood
%A Paulina Valenzuela C
%A Cecilia Bustos A
%A Jean Pierre Lasserre
%A William Gacit¨²a E
%J MADERAS : Ciencia y Tecnolog¨ªa
%D 2012
%I Universidad del B¨ªo-B¨ªo
%X El objetivo de este trabajo fue localizar el m¨ªnimo volumen en ¨¢rboles de E. nitens que caracterice el comportamiento mec¨¢nico y anat¨®mico para un muestreo no destructivo. Los ¨¢rboles fueron cortados desde Mulch¨¦n y Yungay en la regi¨®n del B¨ªo-B¨ªo. Se establecieron relaciones entre las propiedades nanomec¨¢nicas y la anatom¨ªa de la madera con el agrietamiento y las fracturas mayores (rajaduras). Se obtuvieron los par¨¢metros raz¨®n de ductilidad (E/H) y m¨®dulo de resiliencia (u r), medidos en la capa S2 y lamela media. Los resultados mostraron que el volumen representativo de los ¨¢rboles de E. nitens se encontraban a 3 metros de altura desde la base de los ¨¢rboles y desde el anillo 5 al 7. Al mismo tiempo, se logr¨® establecer que la lamela media es m¨¢s fr¨¢gil que la capa S2 de la pared celular. Se determin¨® una relaci¨®n entre la caracterizaci¨®n de los vasos y el nivel de agrietamiento de la madera. Esto es, a mayor ¨¢rea y di¨¢metro de los vasos y a menor n¨²mero de ¨¦stos, el nivel de agrietamiento fue mayor. Las grietas se concentraron principalmente en los primeros metros de altura del ¨¢rbol, existiendo una buena relaci¨®n con el E/H de la lamela media, que mostr¨® un cambio significativo a los 3 metros de altura. Las grietas en los anillos de crecimiento se centraron notoriamente en madera de temprana y en los anillos del 5 al 7 (desde m¨¦dula a corteza). The aim of this study was to define the minimum volumen in trees of E. nitens that characterize the mechanical and anatomy behavior for non-destructive sampling. The trees were cut from sites located in Mulchen and Yungay in the region of B¨ªo B¨ªo. Relationships were found between nanomechanical properties, wood anatomy and wood cracks and fractures. The response variables were the ductility ratio (E/H) and the modulus of resilience (u r), in the S2 layer and middle lamella. The results showed that the representative volume, from E. nitens families is at 3 meter high from base of the trees and between the 5th to 7th annual rings. Also, it was established that the middle lamella is more brittle than the S2 layer. Relationship between the vessels morphology and the level of the wood cracking was observed. A high area of vessels, a high vessel diameter and a small frequency of them, resulted in high cracking. The cracks were mainly concentrated in the first meters of tree, were we found a good relationship of this response variable with the E/H ratio for the middle lamella; there was a significant change of this ratio at 3 meters high. Cracks were evident on earlywood and from the 5th to the 7th annual rings.
%K Propiedades mec¨¢nicas
%K nanoindentaciones
%K anatom¨ªa de la madera
%K ultraestructura de la madera
%K fracturas
%K Nanomechanical properties
%K nanoindentations
%K wood anatomy
%K wood ultrastructure
%K cracks
%U http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-221X2012000300006