%0 Journal Article
%T Cercet ri privind cinetica  i mecanismul coroziunii arm turii de o el zincat termic
%A Andreea Hegyi
%J Urbanism. Arhitectura. Constructii
%D 2011
%I NR&DI URBAN-INCERC
%X The paper summarizes experimental results on the corrosion of hot-dip galvanized steel  n concrete. To this purpose the experimental tests were effectuated on kinetics and mechanism corrosion of rebars placed  n electrolytes simulating the solution  n concrete pores and fresh concrete during its hardening. The electrochemical analysis methods were studied the corrosion kinetics and mechanism and using optical microscopy and X-ray diffraction revealed the formation of calcium hydroxizincate on hot-dip galvanized steel reinforcement surface. The results showed a better corrosion behavior of hot dip galvanized steel reinforcement  n an environment as close to pH 12.5 and while formation the calcium hydroxizincate passivating layer.
%K corrosion
%K reinforced concrete
%K hot dip galvanized rebar
%U http://uac.incd.ro/Art/v2n1a05.pdf