%T Nanos¨ªlice como carga en la RTV SR usada para cubrir aisladores/ Nanosilica as filler in the Room temperature vulcanized silicone rubber used to coat insulators
%A Ignat P¨¦rez Almirall
%A Daniella Cibele Bezerra
%A Miguel Castro Fern¨¢ndez
%A Edson Guedes da Costa.
%J Ingenier¨ªa Energ¨¦tica
%D 2012
%I 
%X En el presente trabajo se realiza un estudio sobre la influencia que tiene agregar como carga nanos¨ªlice a la goma de silicona vulcanizada a temperatura ambiente (RTV SR, por sus siglas en ingl¨¦s) que es empleada para cubrir aisladores de vidrio o de porcelana. Con este objetivo se observ¨® la dispersi¨®n de la nanos¨ªlice en la RTV SR por medio de microscop¨ªa electr¨®nica de barrido (MEV, por sus siglas en ingl¨¦s), se midi¨® la permitividad de la RTV SR con y sin nanos¨ªlice para varias frecuencias y se evalu¨® la influencia que tiene la nanos¨ªlice en la resistencia a la erosi¨®n. Adem¨¢s fueron medidas las corrientes de fuga durante ensayos de niebla salina a aisladores de vidrio pintados con estos recubrimientos, analizando tambi¨¦n la p¨¦rdida de hidrofobicidad que ocurre durante el ensayo y su recuperaci¨®n una vez finalizado el mismo.The present research work carries out a study on the influence of nanosilica on room temperature vulcanized silicone rubber (RTV SR) used to coat insulators. Considering this objective, the dispersion of nanosilica was observed by means of scanning electron microscopy (MEV), the permittivity of the room temperature vulcanized silicone rubber was measured with and without nanosilica for different frequencies and the influence of nanosilica in erosion resistance. Leakage currents were also measured during salt spray tests to glass insulators covered with these coatings; the loss of hidrophobicity during the test was also measured and its recovery was analyzed the test was finished.
%K Recubrimientos de silicona vulcanizada a temperatura ambiente
%K nanocargas
%K corrientes de fuga
%K erosi¨®n
%K hidrofobicidad
%K Room temperature vulcanized silicone rubber coatings
%K nanofillers
%K leakage currents
%K erosion
%K hidrophobicity