%T Caracter¨ªsticas f¨ªsicas y composicionales de pastas de gres porcel¨¢nico con arcillas de Teruel
%A Lazaro
%A A.
%A Garc¨ªa Portilo
%A C.
%A De la Torre
%A J.
%A Bastida
%A J.
%J Bolet¨ªn de la Sociedad Espa£¿ola de Cer¨¢mica y Vidrio
%D 2012
%I Sociedad Espa?ola de Cer¨¢mica y Vidrio
%R 10.3989/cyv.292012
%X Stoneware pots were produced in the temperature range 1120-1220 using as raw materials ball clays from the mining area of Teruel (Spain) with additions of feldspars and without quartz additions. Data about water absorption, shrinkage, flexural strength and colour space (L a* b*) are provided, as well as semiquantitative estimations of the crystalline phases in the bodies using the reference intensity method. The results fulfil the norm ISO-13006 regarding water absorption and mechanical strength at 1185 ¡ãC. In addition, it is shown that the intensity reference method was a good alternative to more advanced quantitative methods. Se desarrollaron pastas de gres porcel¨¢nico, elaboradas con arcillas de la zona minera de Teruel, con adiciones de feldespatos comerciales y sin adici¨®n de cuarzo, en el intervalo de temperatura 1120-1220. Se incluyen datos de absorci¨®n de agua, contracci¨®n lineal, resistencia a flexi¨®n y determinaciones de blancura (L a* b*), as¨ª como estimaciones semicuantitativas de fases cristalinas por el m¨¦todo de las intensidad de referencia. Se obtuvieron resultados cumpliendo con la norma ISO -13006 respecto a absorci¨®n de agua y resistencia mec¨¢nica a 1185 ¡ãC. Adem¨¢s, se demostr¨® la conveniencia del m¨¦todo de las intensidades de referencia como alternativa a m¨¦todos cuantitativos m¨¢s avanzados.
%K Raw materials
%K stoneware
%K ball clays
%K Teruel
%K semiquantitative analysis
%K Materias primas
%K gres porcel¨¢nico
%K ball clays
%K Teruel
%K an¨¢lisis semicuantitativo