%T Comportamiento mec¨¢nico de materiales masivos superconductores de segunda generaci¨®n en funci¨®n de la temperatura
%A K. Konstantopoulou
%A J. Y. Pastor
%A J. J. Roa
%A M. Segarra
%J Ci¨ºncia & Tecnologia dos Materiais
%D 2010
%I Scientific Electronic Library Online
%X En este trabajo se han analizado dos materiales masivos superconductores de base YBaCuO, con el objetivo de estudiar la influencia del m¨¦todo de procesado (m¨¦todo Bridgman y m¨¦todo Top-Seeding Melt Growth) y de la temperatura de ensayo en su comportamiento mec¨¢nico. Ambos materiales se ensayaron a temperatura ambiente (300 K) y a baja temperatura (77 K), determinandose la resistencia mec¨¢nica y la tenacidad a fractura en flexi¨®n en tres puntos. Adem¨¢s, en uno de los materiales, que presentaba anisotrop¨ªa microestructural, se realizaron ensayos en las dos direcciones microestructuralmente m¨¢s relevantes. Los resultados obtenidos muestran que el comportamiento mec¨¢nico del material est¨¢ controlado por los defectos y grietas introducidas durante el procesado y, por lo tanto, si se quiere mejorar las propiedades, deber¨ªa reducirse la cantidad y el tama o de estas imperfecciones. In the present study, have been researched two superconductor bulk materials of YBaCuO, with the aim of analyzing the influence of the processing method (Bridgman and Top-Seeding Melt Growth) and the test temperature in their mechanical behaviour. Both of them have been tested at room temperature (300 K) and at service temperature (77 K). Three point bending tests have been carried out, in order to measure the mechanical strength and the fracture toughness. Moreover, one of the two materials, which present transversal microstructural anisotropy, has been tested for the both more relevant directions. The obtained results show that the mechanical behaviour of the material is controlled by the defects and cracks, that have been introduced during the processing and therefore, in order to improve the mechanical properties, the amount and the size of the defects should be reduced.
%K YBaCuO
%K comportamiento mec¨¢nico
%K superconductores
%K criogenia
%K YBaCuO
%K mechanical behaviour
%K superconductors
%K cryogenic
%U http://www.scielo.oces.mctes.pt/scielo.php?script=sci_arttext&pid=S0870-83122010000200007