%0 Journal Article
%T Avalia  o da fotodegrada  o de ABS exposto a condi  es naturais
%A R. M. Santos
%A G. Botelho
%A A. V. Machado
%J Ci¨ºncia & Tecnologia dos Materiais
%D 2010
%I Scientific Electronic Library Online
%X Amostras de acrilonitrilo-butadieno-estireno (ABS) foram submetidas a envelhecimento sob condi  es naturais, durante 4 meses em Lisboa, para avaliar a sua estabilidade ¨¤ radia  o ultravioleta (UV). A degrada  o que ocorre ¨¤ superf¨ªcie das amostras foi analisada por Espectroscopia de Infravermelhos com um Acess¨®rio de Reflex o Total Atenuada (FTIR-ATR) e determinou-se o decr¨¦scimo do componente butadi¨¦nico como indicador do grau de degrada  o. Correlacionaram-se as altera  es qu¨ªmicas na superf¨ªcie com a perda de propriedades mecanicas. A degrada  o ao longo da espessura foi estudada por espectroscopia de IR acoplada com microsc¨®pio. Verificou-se que para o tempo de exposi  o em causa, o decr¨¦scimo acentuado do butadieno ocorreu apenas ¨¤ superf¨ªcie, indicando que o decr¨¦scimo da capacidade de alongamento do ABS durante o processo de degrada  o ¨¦ tamb¨¦m devido ¨¤ forma  o e propaga  o de fissuras para o interior das amostras. Natural weathering of acrylonitrile-butadiene-styrene (ABS) was performed in Lisbon during 4 months in order to evaluate its stability to UV radiation. Surface characterization of photodegraded ABS samples was investigated by infrared spectroscopy with attenuated total reflectance accessory (FTIR-ATR) and the decrease of polybutadiene (PB) component was used as an indicator of the degradation degree. A correlation between chemical modifications on surface and mechanical properties loss was made. Infrared spectroscopy coupled to microscope was used to study degradation along sample thickness. It was noticed that for this sample a drastic decrease of PB occurred only at the surface, which indicate that the decrease of elongation capability of ABS during degradation process is also due to the cracks formation and its propagation along the thickness.
%K Acrilonitrilo-butadieno-estireno
%K Degrada  o foto-oxidativa
%K Modifica  es qu¨ªmicas
%K Propriedades Mecanicas
%K Acrylonitrile-butadiene-styrene
%K Photo-oxidative degradation
%K Chemical changes
%K Mechanical Properties
%U http://www.scielo.oces.mctes.pt/scielo.php?script=sci_arttext&pid=S0870-83122010000100009