%T Improvement to the Corrosion Resistance of Ti-Based Implants Using Hydrothermally Synthesized Nanostructured Anatase Coatings
%A Martina Lorenzetti
%A Eva Pellicer
%A Jordi Sort
%A Maria Dolors Bar¨®
%A Janez Kova£¿
%A Sa£¿a Novak
%A Spomenka Kobe
%J Materials
%D 2014
%I MDPI AG
%R 10.3390/ma7010180
%X The electrochemical behavior of polycrystalline TiO 2 anatase coatings prepared by a one-step hydrothermal synthesis on commercially pure (CP) Ti grade 2 and a Ti13Nb13Zr alloy for bone implants was investigated in Hank¡¯s solution at 37.5 ¡ãC. The aim was to verify to what extent the in-situ-grown anatase improved the behavior of the substrate in comparison to the bare substrates. Tafel-plot extrapolations from the potentiodynamic curves revealed a substantial improvement in the corrosion potentials for the anatase coatings. Moreover, the coatings grown on titanium also exhibited lower corrosion-current densities, indicating a longer survival of the implant. The results were explained by considering the effects of crystal morphology, coating thickness and porosity. Evidence for the existing porosity was obtained from corrosion and nano-indentation tests. The overall results indicated that the hydrothermally prepared anatase coatings, with the appropriate morphology and surface properties, have attractive prospects for use in medical devices, since better corrosion protection of the implant can be expected.
%K titanium dioxide crystalline coating
%K corrosion resistance
%K nanomechanical behavior
%K biomaterials
%U http://www.mdpi.com/1996-1944/7/1/180