%T Fe3O4-FeO基熔铁催化剂费–托合成反应性能
Performances of Fe3O4-FeO Based Fused Iron Catalysts for Fischer-Tropsch Synthesis
%A 杨霞珍
%A 夏航
%A 霍超
%A 刘化章
%J Clean Coal and Energy
%P 7-13
%@ 2334-3516
%D 2015
%I Hans Publishing
%R 10.12677/CCE.2015.32002
%X
在固定床反应器中进行了反应温度、压力、空速、氢碳比、粒度对Fe3O4-FeO基(nFe2+/nFe3+ = 0.89 - 1.5)熔铁催化剂费–托合成反应性能的影响研究。实验结果表明,该熔铁催化剂低温活性良好,在493 K时,CO转化率51.93%。通过降低氢碳比、温度或空速,或升高反应压力,可以减小甲烷选择性,特别是温度的影响作用结果明显,由5.80%降至2.99%。催化剂粒度小于0.1 mm消除了在固定床中的内扩散影响。反应条件对Fe3O4-FeO基熔铁催化剂F-T合成反应性能影响规律和其它铁基催化剂F-T合成类似。<br/>The effects of reaction temperature, pressure, space velocity, H2/CO ratio and particle size on per-formances of Fe3O4-FeO based fused iron catalysts for Fischer-Tropsch synthesis have been inves-tigated in a fixed-bed reactor. The results show that, the activity of the catalysts was well at low temperature. Conversion of carbon monoxide was 51.93% at 493 K. The selectivity of methane could be decreased by lowering the H2/CO ratio, temperature or space velocity, or increasing the pressure. Especially, the selectivity of methane was decreased from 5.80% to 2.99% by reducing temperature. The inner diffusion was eliminated when the particle size was less than 0.1 mm in the fixed-bed reactor. The effects of reaction conditions on Fe3O4-FeO based fused iron catalysts for Fischer-Tropsch synthesis were found to be similar to the other iron catalysts for Fischer- Tropsch synthesis.
%K 低温,固定床,熔铁催化剂,费–托合成
Low Temperature
%K Fixed-Bed Reactor
%K Fused Iron Catalyst
%K Fischer-Tropsch Synthesis
%U http://www.hanspub.org/journal/PaperInformation.aspx?PaperID=15585