%0 Journal Article
%T 溶剂热法制备LaF3:Ce3+/Tb3+晶体及功能化
Synthesis of LaF3:Ce3+/Tb3+ Crystals via Solvothermal Method and Functionalization
%A 张艺
%J Studies in Synthetic Chemistry
%P 19-23
%@ 2332-7960
%D 2015
%I Hans Publishing
%R 10.12677/SSC.2015.32003
%X
采用溶剂热法,乙醇和乙二醇为混合溶剂,160℃条件下,反应12小时,成功制备了LaF3:Ce3+/Tb3+晶体。并用聚丙烯酸(PAA)对材料进行了功能化,红外吸收光谱显示材料表面成功修饰上羧基(-COOH)。以275 nm为激发波长,LaF3:Ce3+/Tb3+及COOH-LaF3:Ce3+/Tb3+晶体的发射波长均为526 nm,而功能化的LaF3:Ce3+/Tb3+荧光强度较低。
The LaF3:Ce3+/Tb3+ crystals were prepared using solvothermal method, at 160?C for 12 h in the mixed solvents of ethanol and glycol. The as-prepared LaF3:Ce3+/Tb3+ crystals were functionlized with Poly(acrylic acid). IR absorption spectra showed that the carboxyl group (-COOH) is on the surface of LaF3:Ce3+/Tb3+ crystals. Under 275 nm excitation, the emission peaks of LaF3:Ce3+/Tb3+ and COOH-LaF3:Ce3+/Tb3+ crystals locate at 526 nm. Moreover, the fluorescent intensity of the functional LaF3:Ce3+/Tb3+ is lower.
%K 溶剂热法,聚丙烯酸(PAA),功能化材料,LaF3