%T Improvement of Thermal Stability of Nd-Tb-Fe-Co-B Sintered Magnets by Additions of Pr, Ho, Al, and Cu
%A A. A. Lukin
%A E. I. Il'yashenko
%A A. T. Skjeltorp
%A G. Helgesen
%J Physics Research International
%D 2012
%I Hindawi Publishing Corporation
%R 10.1155/2012/416717
%X The present work investigates the influence of Pr, Al, Cu, B and Ho which were introduced into the Co-containing sintered magnets of Nd-Dy-Tb-Fe-Co-B type on the magnetic parameters (, , , max). The effect of heat treatment parameters on magnetic properties was also studied. It was revealed that the essential alloying of NdFeB magnets by such elements as Dy, Tb, Ho, Co as well as by boron-forming elements, for example, by titanium, may lead to reducing of F-phase quantity, and, as a consequence, to decreasing of magnetic parameters. It was also shown that additional doping of such alloys by Pr, B, Al and Cu leads to a significant increase of the quantity of F-phase in magnets as well as solubility of the Dy, Tb, Ho and Co in it. This promotes the increase of magnetic parameters. It was possible to attain the following properties for the magnets (Nd0,15Pr0,35Tb0,25Ho0,25)15(Fe0,71Co0,29)bal · Al0,9Cu0,1B8,5 (at. %) after optimal thermal treatment {1175 K (3,6–7,2 ks) with slow (12–16 ks) cooling to 675 K and subsequently remaining at =775 K for 3,6 ks—hardening}: =0,88 T, =1760 kA/m, max=144 kJ/m3, <|0,01|%/K in the temperature interval 223–323 K.
%U http://www.hindawi.com/journals/phys/2012/416717/