%T A New Strategy for the Use of Post-Processing Vacuum Bags from Aerospace Supplies: Nucleating Agent to LLDPE Phase in PA6/LLDPE Blends
%J Recycling | An Open Access Journal from MDPI
%D 2019
%R https://doi.org/10.3390/recycling4020018
%X In the aerospace industry, many composite parts are manufactured by processes using plastic vacuum bags made of polyamide 6 (PA6) as a consumable material. This implies that after demolding the part, this plastic material should be discarded, generating a considerable amount of waste. Tons of vacuum bags are discarded and incinerated per month by several companies in this sector, which highlights the need to recycle and/or reuse this material. PA6/linear low-density polyethylene (LLDPE) blends are of great technological interest because they can combine the excellent thermo-mechanical and oxygen barrier properties of the PA6 with high impact strength, good processability, and low cost of LLDPE. The replacement of neat PA6 by the post-processing vacuum bags residue PA6 may be a new strategy for the recycling of this material. In this work, PA6/LLDPE/maleic anhydride-grafted LLDPE (LLDPE- g-MA) (90/5/5) blends were prepared using a co-rotational twin-screw extruder and the neat PA6 was replaced by different contents of post-processing PA6 (5, 10, 15 and 20 wt.%). The mechanical, thermal, and morphological characterization was evaluated. The increase in the content of post-processing PA6 caused an increase in the crystallinity degree of the LLDPE phase, acting as a nucleating agent to the LLDPE phase, reducing the toughening effect of this phase in the blends and, therefore, providing this phase to act as a reinforcing agent. View Full-Tex
%U https://www.mdpi.com/2313-4321/4/2/18