%T Al<sub>x</sub>CoCrFeNi高熵合金组织性能研究<br>Research on Microstructure and Properties of Al<sub>x</sub>CoCrFeNi High-Entropy Alloy
%A 马金磊
%A 孟祥然
%A 曲涛
%J Advances in Material Chemistry
%P 66-70
%@ 2331-0146
%D 2021
%I Hans Publishing
%R 10.12677/AMC.2021.92008
%X 采用激光烧结法制备Al<sub>x</sub>CoCrFeNi (x = 1; 1.5; 2)高熵合金，通过测试其显微组织、成分和力学性能，研究Al元素含量的变化对高熵合金的组织性能的影响。实验结果表明，当x从1到1.5再到2不断增大时，Al<sub>x</sub>CoCrFeNi合金的晶体结构由FCC + BCC向BCC不断转变，高熵合金的晶格畸变和硬度也随之增大；当x = 2时晶格畸变达到最大，同时硬度也达到最大值512.5 HV。<br />
Al<sub>x</sub>CoCrFeNi (x = 1; 1.5; 2) high-entropy alloy was prepared by laser sintering. The effect of Al content on the microstructure and properties of high-entropy alloy was studied by measuring its microstructure, composition and mechanical properties. The experimental results show that when x increases from 1 to 1.5 and then to 2, the crystal structure of Al<sub>x</sub>CoCrFeNi alloy changes from FCC + BCC to BCC, and the lattice distortion and hardness of the high entropy alloy also increase; the lattice distortion reaches its maximum when x = 2, and the hardness also reaches the maximum of 512.5 HV.
%K 高熵合金，硬度，组织结构<br>High Entropy Alloys
%K Hardness
%K Structure