EVALUATION OF MICROSTRUCTURAL STABILITY OF DISSIMILAR WELD JOINTS

The microstructural changes occurring in the weld joint P92/316Ti during his long-term exposure at high temperature were studied. In parallel to experiments were carried out calculations of phase equilibria for the base materials and the weld joint using the ThermoCalc software. Based on the experimental results and computational modeling results were evaluated a microstructural stability and the application of the base materials and the weld joint.