Tensiones de contacto por el método de elementos finitos del acero AISI 1045 endurecido por rodillo

In this paper, the tense-deformational behavior is analyzed by means of simulation using the finite element method for AISI 1045 cold rolled deformed steel. ANYSYS V.10 software was used in this study. Revolution number, compressive strength and tool feed rate were the variables considered in the deformation process. They allowed determining the contact stress of the deformed material. The material used was 30 mm diameter and 100 mm length. Samples of 30 mm diameter and 3 mm thickness were prepared for the optical microscopic observation, which were compared to the results obtained from the simulation. The tensile status of the deformed samples was evaluated as from the reduction of the average size of the grains as per the strength applied. This study intends to show that the cold hardening method is a surface hardening option. En el trabajo se analiza el estado tenso-deformacional mediante la simulación por el método de los elemento finitos del acero AISI 1045 deformado en frío empleando rodillo simple, para ello se utilizó el software ANSYS V.10. En el proceso de deformación se consideran las variables número de revolución, la fuerza compresiva y el avance de la herramienta, lo que permitió determinar las tensiones de contacto del material deformado. El diámetro del material empleado fue de 30 mm con una longitud de 100 mm. Para la observación de la microscopía óptica, se prepararon muestras de 30 mm de diámetro por 3 mm de espesor, las que fueron comparadas con los resultados obtenidos de la simulación. El estado tensional de las muestras deformadas se evaluó a partir de la reducción del tama o promedio de los granos según la fuerza empleada. Con el desarrollo del trabajo se trata de demostrar que el empleo del método de endurecimiento en frío es una alternativa de endurecimiento superficial.