Evaluación del trabajo esencial de fractura en chapa de un acero de alta resistencia de fase dual

Fracture toughness of advanced high strength steels (AHSS), can be used to optimize crash behavior of structural components. However it cannot be readily measured in metal sheet because of the sheet thickness. In this work, the Essential Work of Fracture (EWF) methodology is proposed to evaluate the fracture toughness of metal sheets. It has been successfully applied in polymers films and some metal sheets. However, their information about the applicability of this methodology to AHSS is relatively scarce. In the present work the fracture toughness of a Dual Phase (strength of 800 MPa) and drawing steel sheets has been measured by means of the EWF. The results show that the test requirements are met and also show the clear influence of notch radii on the measured values, specially for the AHSS grade. Thus, the EWF is postulated as a methodology to evaluate the fracture toughness in AHSS sheets. La tenacidad de fractura de aceros de alta resistencia (AHSS), es una propiedad interesante para optimizar el comportamiento a impacto, pero su caracterización experimental en chapas metálicas es compleja debido a su espesor. En este trabajo se plantea el método del Trabajo Esencial de Fractura (TEF), como alternativa al cálculo de la tenacidad. Este método ya ha sido utilizado con éxito en polímeros y aceros dúctiles, aunque la información sobre su aplicación en AHSS es escasa. Se ha evaluado la tenacidad en un acero de fase dual de 800 MPa de resistencia y se ha comparado con la de un acero de embutición. Los resultados muestran que se cumplen los requisitos del método y ponen en evidencia la influencia del radio de entalla en el valor obtenido de TEF, especialmente para AHSS. Con todo ello, el método TEF se puede usar para caracterizar la tenacidad de AHSS en formato chapa.