Dynamic deformation of high pressure die-cast magnesium alloys

The dynamic behavior of the die-cast Mg-6 % Al-0.5 % Mn and Mg-9 % Al-1 % Zn alloys has been investigated in a wide range of temperatures and compared to the quasi-static behavior. It has been found that, at high strain rates, these alloys possess very good energy absorption capacity and that twinning is significantly enhanced. The small variability in the tensile ductility at dynamic rates is attributed to the independence of the adiabatic shear failure mechanism of the porosity distribution. El comportamiento dinámico de las aleaciones de magnesio Mg-6 % Al-0,5 % Mn y Mg-9 % Al-1 % Zn ha sido investigado en un amplio intervalo de temperaturas y se ha comparado con el comportamiento cuasi-estático. Se ha encontrado que, a altas velocidades de deformación estas aleaciones poseen alta capacidad de absorción de energía y que se mejora el maclado significativamente. Las peque as variaciones en la ductilidad a tracción a velocidades dinámicas se atribuyen a la independencia de de los mecanismos de cizalla adiabática de la distribución de la porosidad.