Taladrado por fricción en aceros de doble fase

This work describes the experimental study of the friction drilling process in dual phase (DP) steels, with yield strengths from 600 to 800 Mpa. The optimal machining conditions with different thicknesses was assessed through controlled tests at different rotation speeds and feed rates. On one hand, the torque and the thrust force were computed and monitorized. On the other hand, the dimensional tolerances of the holes were evaluated. Another topic of interest inherent to this special technique is the temperature level reached during the friction process which is crucial when it comes to development of microstructural transformations. This thermal condition can transform the mechanical properties of material near the hole and the burr. En este trabajo se expone un estudio del proceso de taladrado por fricción en chapas de diferentes aceros de doble fase (DP), con límites elásticos variables desde 600 hasta 800 MPa. Se realiza una evaluación de las condiciones óptimas de mecanizado en función del material y el espesor empleado, variando las velocidades de giro y los avances de penetración. Al mismo tiempo se monitoriza el par y la fuerza axial resultante, analizando además el espesor de la rebaba en distintas profundidades, es decir, las tolerancias dimensionales generadas por el proceso. Otro punto de interés es la medición de la temperatura alcanzada durante el proceso como consecuencia de la fricción, ya que la cantidad de calor absorbido por la pieza puede influir en las transformaciones microestructurales que el material experimenta. Esta afectación térmica puede transformar las propiedades mecánicas del material en las cercanías del agujero y en la rebaba.