Estudio de los mecanismos de descomposición isotérmica de austenita en perlita en un acero 0,44C-0,73Mn

The goal of this paper is to determine the austenite-to-pearlite isothermal decomposition mechanisms in a 0.44C-0.73 Mn steel. More precisely, the role of austenitizing temperature (Tγ), and hence the austenitic grain size (AGS), in the kinetics of pearlite formation has been studied. Results allow us to conclude that the average size of pearlitic colonies is increased as the AGS is increased. On the other hand, it appears that the interlamellar spacing of the pearlite does not depend on the Tγ but is controlled by the isothermal decomposition temperature of austenite (T). Finally, it was found that formation of pearlite is triggered for small AGS values and isothermal decomposition temperature regimes where the predominant controlling mechanism is due to carbon volume diffusion. El objetivo de este trabajo se centra en el estudio de los mecanismos de descomposición isotérmica de la austenita en perlita en un acero de composición 0,44C-0,73 Mn. En particular, se estudia cómo afecta la temperatura de austenización (Tγ), y por tanto, el tama o de grano austenítico de partida (TGA), en la cinética de formación de la perlita. Se ha comprobado que existe una relación directa entre Tγ y el tama o medio de las colonias perlíticas. Por el contario, el espaciado interlaminar perlítico no depende de Tγ, sino que está controlado por la temperatura de descomposición isotérmica (T), de la austenita en perlita. Finalmente se ha observado que la cinética de formación de perlita se ve acelerada para el caso de TGA peque os y cuando el mecanismo predominante en el rango de temperaturas de trabajo es la difusión en volumen del carbono.