Corrosion behavior of Fe3Al intermetallics with addition of lithium, cerium and nickel in 2.5 % SO2+N2 at 900 °C

The corrosion behavior of Fe3Al-type intermetallic alloys with addition of 1 at. % cerium, lithium and nickel at high temperature has been studied. The various alloys were exposed to an environment composed of 2.5 % SO2+N2 at 900 °C for 48 h. For all the intermetallic tested, the corrosion kinetics showed a parabolic behavior. The alloy, which showed less corrosion rate, was the Fe3AlNi alloy, being Fe3AlCeLi the alloy with the highest corrosion rate. For the various alloys, energy dispersive X-ray spectroscopy analysis, EDS, on the developed scale only detected aluminum, oxygen, and traces of iron and cerium, suggesting the formation of alumina as main component. The intermetallic alloys showed oxide cracking and spalling. The intermetallic chemical composition played an important role in defining the oxide scale morphology and the extent of damage. Se estudió el comportamiento a la corrosión a alta temperatura de intermetálicos tipo Fe3Al con adición de 1at. % de cerio, litio y níquel. Las diferentes aleaciones fueron expuestas bajo un ambiente compuesto de 2,5 % SO2+N2 a 900 °C durante 48 h. Para todos los intermetálicos ensayados, la cinética de corrosión presentó un comportamiento parabólico. La aleación que mostró la menor velocidad de corrosión fue el intermetálico Fe3AlNi, siendo el intermetálico Fe3AlCeLi el de mayor velocidad de corrosión. Los análisis mediante espectroscopía de dispersión de rayos X, EDS, sobre la costra formada identificaron únicamente aluminio, oxígeno y trazas de hierro y cerio, lo que sugiere la formación de alúmina como el componente principal. Los intermetálicos mostraron agrietamiento y desprendimiento de la costra de óxido. La composición química de los intermetálicos tuvo un papel importante en la definición de la morfología del óxido formado y el grado de da o.