Análisis de los transitorios de ruido electroquímico para aceros inoxidables 316 Y – DUPLEX 2205 en NaCl Y FeClKeywords: Pitting corrosion , Electrochemical noise , Electrochemical Techniques , Stainless steel austenitic 316 , SS Duplex 2205 , Corrosión por picaduras , Ruido electroquímico , Técnicas electroquímicas , Acero inoxidable austenítico 316 , Acero inoxidable Dúplex 2205 Abstract: This work shows the results obtained from electrochemical noise measurements for different materials exhibiting pitting corrosion. The transients presented in the potential and current time, correlates with the scanning electron microscopy (SEM) surface analysis. Electrochemical measurements were made at different exposure times to obtain the correlation. The materials used were stainless steel austenitic 316 and duplex 2205, immersed in ferric chloride (FeCl3) and sodium chloride (NaCl) electrolytes. SEM analysis shows that the transients observed in the time series, really correspond to the activity of pit nucleation developed over the surface of the electrodes. En este trabajo se muestran los resultados obtenidos de las mediciones de ruido electroquímico para diferentes materiales que exhiben corrosión por picaduras. Los transitorios presentados en las series de tiempo en corriente y en potencial, se correlacionan con el análisis superficial de microscopía electrónica de barrido (MEB). Las mediciones electroquímicas fueron realizadas a diferentes tiempos de exposición, para obtener una correlación. Los materiales usados fueron los aceros inoxidables 316 y dúplex 2205, inmersos en cloruro férrico (FeCl3) y cloruro de sodio (NaCl) como electrolitos. Los análisis por MEB, muestran que los transitorios observados en las series de tiempo, corresponden realmente con la actividad de la nucleación de picaduras desarrollada sobre la superficie de los electrodos.
|