Distribution of lead and silver under lead blast furnace conditions

Two experimental studies of metal solubility in slags were carried out at 1473 K (1200 °C). In the first one the solubility of lead in the PbO-ZnO-CaO-SiO2-“Fe2O3” slag system under a reducing atmosphere (PCO/PCO2 = 2.45) was studied. In the second part, slags of the CaO-SiO2-“Fe2O3” system were equilibrated with Pb - 1.3 mass % Ag alloys under an inert atmosphere. In both cases the CaO/SiO2 mass ratio was from 1.0 to 1.6 and Fe/SiO2 mass ratio was 1.1 and 1.7. The lead solubility in the slags of both experimental parts diminishes with increasing the slag basicity (CaO/SiO2) and diminishing the Fe/SiO2 ratio. Lead oxide is the only compound that can be reduced under the reducing atmosphere and at the temperature at the tuyeres level, 1473 K. Silver solubility in slags decreases with increasing both CaO/SiO2 and Fe/SiO2 ratios in the slags of the CaO-SiO2-“Fe2O3” system. Se realizaron dos estudios experimentales de solubilidad de metal en escorias a 1.473 K (1.200 °C). En el primero se estudió la solubilidad de plomo en el sistema PbO-ZnO-CaO-SiO2-“Fe2O3” bajo una atmósfera reductora (PCO/PCO2 = 2,45). En la segunda parte, escorias del sistema CaO-SiO2-“Fe2O3” fueron equilibradas con aleaciones Pb - 1,3 % Ag en atmósfera inerte. En ambos casos la relación CaO/SiO2 fue variada de 1.0 a 1.6 y la relación Fe/SiO2 fue de 1,1 y 1,7. La solubilidad de plomo en las escorias de ambas etapas experimentales disminuye con el incremento de la basicidad (CaO/SiO2) y la disminución de la relación Fe/SiO2. El óxido de plomo es el único compuesto que puede ser reducido bajo la atmósfera reductora y a la temperatura en el nivel de las toberas del horno alto, 1.473 K. La solubilidad de la plata en la escoria decrece con el aumento de las relaciones CaO/SiO2 y Fe/SiO2 en las escorias del sistema CaO-SiO2-“Fe2O3”.