Large-size 0.1 Yb 2O 3–1.0 Al 2O 3–98.9 SiO 2 (mol%) core glass was prepared by the sol–gel method. Its optical properties were evaluated. Both large mode area double cladding fiber (LMA DCF) with core diameter of 48 μm and large mode area photonic crystal fiber (LMA PCF) with core diameter of 90 μm were prepared from this core glass. Transmission loss at 1200 nm is 0.41 dB/m. Refractive index fluctuation is less than 2 × 10 ？4. Pumped by 976 nm laser diode LD pigtailed with silica fiber (NA 0.22), the slope efficiency of 54% and “light-to-light” conversion efficiency of 51% were realized in large mode area double cladding fiber, and 81 W laser power with a slope efficiency of 70.8% was achieved in the corresponding large mode area photonic crystal fiber.
Galvanauskas, A. High power fiber lasers. Opt. Photon. News 2004, 15, 42–47.
[3]
Li, W.; Zhou, Q.; Zhang, L.; Wang, S.; Wang, M.; Yu, C.; Chen, D.; Hu, L. Watt-level Yb-doped silica glass fiber laser with a core made by sol-gel method. Chin. Opt. Lett. 2013, 11, 091601:1–091601:3.
[4]
Wei, T.; Li, J.; Zhu, J. Theoretical and experimental study of transient response of the Yb-doped fiber amplifier. Chin. Opt. Lett. 2012, 10, 040605:1–040605:4.
Poole, S.B.; Payne, D.N.; Mears, R.J.; Fermann, M.E.; Laming, R.I. Fabrication and characterization of low-loss optical fibers containing rare-earth ions. J. Lightwave Technol. 1986, 4, 870–876.
[9]
Dhar, A.; Paul, M.C.; Pal, M.; Mondal, A.K.; Sen, S.; Maiti, H.S.; Sen, R.J. Characterization of porous core layer for controlling rare earth incorporation in optical fiber. Opt. Express 2006, 14, 9006–9015, doi:10.1364/OE.14.009006.
[10]
Sen, S.; Rakhmatullin, R.; Gubaydullin, R.; Poppl, A. Direct spectroscopic observation of the atomic-scale mechanisms of clustering and homogenization of rare-earth dopant ions in vitreous silica. Pysical. Rev. B 2006, 74, 100201:1–100201:4.
[11]
Wang, S.; Li, Z.; Yu, C.; Wang, M.; Feng, S.; Zhou, Q.; Chen, D.; Hu, L. Fabrication and laser behaviors of Yb3+-doped silica large mode area photonic crystal fiber prepared by sol-gel method. Opt. Mater. 2013, 35, 1752–1755.
[12]
Liu, S.; Li, H.; Tang, Y.; Hu, L. Fabrication and spectroscopic properties of Yb3+-doped silica glasses by sol-gel method. Chin. Opt. Lett. 2012, 10, 081601:1–081601:4.
[13]
Chen, G.; Zhang, Q.; Yang, G.; Jiang, Z. Mid-infrared emission characteristic and energy transfer of Ho3+-doped tellurite glass sensitized by Tm3+. J. Fluoresc. 2007, 17, 301–307.
[14]
Charles, C.R.; Fournier, J.T. Coordination of Yb3+ in some inorganic glasses from optical absorption and emission studies. Chem. Phys. Lett. 1969, 3, 517–519.
[15]
Melkumov, M.A.; Bufetov, I.A.; Bubnov, M.M.; Kravtsov, K.S.; Semjonov, S.L.; Shubin, A.V.; Dianov, E.M. Ytterbium lasers based on P2O5- and Al2O3-doped fibers. In Proceedings of the Europeen Conference on Oprical Communication, Stockholm, Sweden, 5–9 September 2004.
[16]
Kirchhof, J.; Unger, S.; Schwuchow, A.; Grimm, S.; Reichel, V. Materials for high-power fiber lasers. J. Non-Cryst. Solids 2006, 352, 2399–2403.
[17]
Li, Y.; Huang, J.; Li, Y.; Li, H.; He, Y.; Gu, S.; Chen, G.; Liu, L.; Xu, L. Optical properties and laser output of heavily Yb-doped fiber prepared by sol-gel method and DC-RTA technique. J. Lightwave Technol. 2008, 26, 3256–3260.
[18]
Andreas, L.; Gerhard, S.; Mario, S.; Thomas, K.; Volker, R.; Stephan, G.; Johannes, K.; Kraused, V.; Georg, R. A new material for high power laser fibers. Proc. SPIE 2008, 6873, 687311:1–687311:9.
[19]
Humbach, O.; Fabian, H.; Grzesik, U.; Haken, U.; Heitmann, W. Analysis of OH absorption bands in synthetic silica. J. Non-Cryst. Solids 1996, 203, 19–23.