Prealloyed (PA) and premixed (PM) W-brass with the composition of 60 wt% W, 1 wt% Ni and 39
wt% brass was sintered at the temperature of 800°C, 920°C and 1000°C each. As a result of difficulties
in the densification of W-Cu and W-Cu alloys, mechanical alloying (MA) and activated sintering
were combined. The powders were mechanically alloyed for 13 hours to produce nanosized W
grains embedded in brass. The microstructure and properties of these composites with increase in
sintering temperature has been studied. Both prealloyed and premixed composites sintered at
800°C (solid state sintering) and 920°C (sub-solidus state sintering) have lower sintered densities
and hardness. The densification rate in the premixed composites was observed to be higher than
that of the prealloyed composites. Their densification and properties increased with the increase
in the sintering temperature. Premixed composite sintered at 1000°C had 91.0% sintered density,
180 Hv microhardness against 76.0% and 133 Hv respectively for prealloyed composite at the
same temperature. The values of electrical conductivity in both prealloyed and premixed composites
increased with increase in temperature.
References
[1]
Mohammed, K.S., Rahmat, A. and Ahmad, K.R. (2012) Sintering Behaviour and Microstructure Evolution of Mechanically Alloyed W-Bronze Composite Powders by Two-Step Ball Milling Process. Journal of Materials Science & Technology, 29, 59-69
[2]
Luo, L.-M., Tan, X.-Y., Lu, Z.-L., Zhu, X.-Y., Zan, X., Luo, G.-N. and Wu, Y.-C. (2014) Sintering Behaviour of W-30 Cu Composite Powder, Prepared by Electroless Plating. International Journal of Refractory Metals and Hard Materials, 42, 51-56. http://dx.doi.org/10.1016/j.ijrmhm.2013.10.012
[3]
Ardestani, M., Rezaie, H.R., Arabi, H. and Razavizadeh, H. (2009) The Effect of Sintering Temperature on Densification of Nanoscale Dispersed W-20-40%wt Cu Composite Powders. International Journal of Refractory Metals and Hard Materials, 27, 862-867. http://dx.doi.org/10.1016/j.ijrmhm.2009.04.004
[4]
Luo, S.-D., Yi, J.-H., Guo, Y.-L., Peng, Y.-D., Li, L.-Y. and Ran, J.-M. (2009) Microwave Sintering W-Cu Composites: Analysis of Densification and Microstructural Homogenization. Journal of Alloys and Compounds, 473, L5-L9. http://dx.doi.org/10.1016/j.jallcom.2008.05.038
[5]
Huang, L.-M., Luo, L.-M., Ding, X.-Y., Luo, G.-N., Zan, X., Cheng, J.-G. and Wu, Y.-C. (2014) Effects of Simplified Pretreatment Process on the Morphology of W-Cu Composite Powder, Prepared by Electroless Plating and Its Sintering Characterization. Powder Technology, 258, 216-221. http://dx.doi.org/10.1016/j.powtec.2014.03.027
[6]
Tang, X.Q., Zhang, H.B., Dua, D.M., Qu, D., Hu, C.F., Xie, R.J. and Feng, Y. (2014) Fabrication of W-Cu Functionally Graded Materials by Spark Plasma Sintering Method. International Journal of Refractory Metals and Hard Materials, 42, 193-199. http://dx.doi.org/10.1016/j.ijrmhm.2013.09.005
[7]
Zhao, P, Guo, S.B., Liu, G.H., Chen, Y.X. and Li, J.T. (2014) Fast Fabrication of W-Cu Functionally Graded Materials by High-Gravity Combustion Synthesis and Melt-Infiltration. Journal of Nuclear Materials, 445, 26-29. http://dx.doi.org/10.1016/j.jnucmat.2013.10.032
[8]
Mondal, A., Upadhyaya, A. and Agrawal, D. (2010) Comparative Study of Densification and microstructural Development in W-18Cu Composites Using Microwave and Conventional Heating. Materials Research Innovations, 14, 355-360. http://dx.doi.org/10.1179/143307510X12820854748638
[9]
Zhou, Y., Wang, K., Liu, R., Wang, X.P., Liu, C.S. and Fang, Q.F. (2012) High Performance Tungsten Synthesized by Microwave Sintering Method. International Journal of Refractory Metals and Hard Materials, 34, 13-17. http://dx.doi.org/10.1016/j.ijrmhm.2012.02.016
[10]
Mondal, A., Upadhyaya, A. and Agrawal, D. (2008) Microwave and Conventional Sintering of Premixed and Prealloyed Tungsten Heavy Alloys. Journal of Materials Science and Technology (MS&T), 8, 2502-2514.
[11]
Hu, K., Li, X.Q., Qu, S.G. and Li, Y.Y. (2013) Spark-Plasma Sintering of W-5.6Ni-1.4Fe Heavy Alloys: Densification and Grain Growth. Metallurgical and Materials Transactions A, 44, 923-933.
[12]
Chen, P.A., Shen, Q., Luo, G.Q., Li, M.J. and Zhang, L.M. (2013) The Mechanical Properties of W-Cu Composite by Activated Sintering. International Journal of Refractory Metals and Hard Materials, 36, 220-224. http://dx.doi.org/10.1016/j.ijrmhm.2012.09.001
[13]
Ibrahim, H., Aziz, A. and Rahmat, A. (2014) Enhanced Liquid-Phase Sintering of W-Cu Composites by Liquid Infiltration. International Journal of Refractory Metals and Hard Materials, 43, 222-226. http://dx.doi.org/10.1016/j.ijrmhm.2013.12.004
[14]
Abu-Oqail, A., Ghanim, M., El-Sheikh, M. and El-Nikhaily, A. (2012) Effects of Processing Parameters of Tungsten- Copper Composites. International Journal of Refractory Metals and Hard Materials, 35, 207-212. http://dx.doi.org/10.1016/j.ijrmhm.2012.02.015
[15]
Zhang, Q.X., Shi, X.L., Yang, H. and Duan, X.L. (2008) Microstructure and Properties of W-15Cu Alloys Prepared by Mechanical Alloying and Spark Plasma Sintering Process. Journal of Wuhan University of Technology-Materials Science Edition, 23., 399-402.
[16]
Meng, Y.F., Shen, Y.F., Chen, C., Li, Y.C. and Feng, X.M. (2014) Effects of Cu Content and Mechanical Alloying Parameters on the Preparation of W-Cu Composite Coating on Copper Substrate. Journal of Alloys and Compounds, 585, 368-375. http://dx.doi.org/10.1016/j.jallcom.2013.09.100
[17]
Mohammed, K.S. and Rahmat, A. (2012) The Role of Activator Rich-W Interboundary Layer on Liquid Phase Sintering of W-Pre-Alloy Bronze Composites of Fe and Co Addition. International Journal of Refractory Metals and Hard Materials, 35, 170-177. http://dx.doi.org/10.1016/j.ijrmhm.2012.04.016
[18]
Yusoff, M., Othman, R. and Hussain, Z. (2011) Mechanical Alloying and Sintering of Nanostructured Tungsten Carbide-Reinforced Copper Composites and Its Characterization. Materials & Design, 32, 3293-3298. http://dx.doi.org/10.1016/j.matdes.2011.02.025
[19]
Kim, J.-C. and Moon, I.-H. (1998) Sintering of Nanostructured W-Cu Alloys Prepared by Mechanical Alloying. Nanostructured Materials, 10, 283-290. http://dx.doi.org/10.1016/S0965-9773(98)00065-8
[20]
Radomysel’skii, I.D., Gaiduchenko, G.K., Kalinyuk, N.N., Medvedovskii, A.B., Nichiporenko, O.S. and Chaikina, N.G. (1983) Effects of Atomization Conditions on the Quality of Bras Powder. Poroshkovaga Metallurgiya, 7, 5-7.
Dovydenkova, A.V., Sergeev, V.L., Chernov, V.A. and Kiseleva, E.V. (1990) Sintering of Brass Powder Having Different Oxygen Contents. Poroshkovaga Metallurgiya, 4, 44-47.
[23]
Daneshjou, K. and Ahmadi, M. (2006) Optimizing the Effective Parameters of Tungsten—Copper Composites. Transactions of the CSME/de la SCGM, 30, 321-327.
[24]
Mondal, A., Upadhyaya, A. and Agrawal, D. (2013) Effects of Heating Mode and Copper Content on the Densification of W-Cu Alloys. Indian Journal of Materials Science, 2013, Article ID: 603791. http://dx.doi.org/10.1155/2013/603791
[25]
Ozkal, B., Upadhyaya, A., Ovecoglu, M.L. and German, R.M. (2004) Realtime Sintering Observations in W-Cu System: Accelerated Rearrangement Densification via Copper Coated Tungsten Powders Approach. Euro PM2004.
[26]
Mondal, A., Agrawal, D. and Upadhyaya, A. (2010) Microwave Sintering of Refractory Metals/Alloys: W, Mo, Re, W-Cu, W-Ni-Cu and W-Ni-Fe. Journal of Microwave Power and Electromagnetic Energy, 44, 28-44.
[27]
Ibrahim, A., Abdallah, M., Mostafa, S.F. and Hegazy, A.A. (2009) An Experimental Investigation on the W-Cu Composites. Materials & Design, 30, 1398-1403. http://dx.doi.org/10.1016/j.matdes.2008.06.068
[28]
Cheng, J.G., Song, P., Gong, Y.F., Cai, Y.B. and Xia, Y.H. (2008) Fabrication and Characterization of W-15Cu Composite Powders by a Novel Mechano-Chemical Process. Materials Science and Engineering: A, 488, 453-457.
[29]
Kung, C., Liao, T.T., Tseng, K.H., Chen, K.Y. and Chuang, M.S. (2009) The Influence of Powder Mixing Process on the Quality of W-Cu Composites. Transactions of the Canadian Society for Mechanical Engineering, 33, 361-375.