终冷温度对Mn系超低碳HSLA钢组织及低温韧性的影响
DOI: 10.11900/0412.1961.2014.00329, PP. 21-30
Keywords: 超低碳低合金高强钢,贝氏体组织,低温韧性,板条块,晶体学特征
Abstract:
研究了终冷温度(550,450和350℃)对Mn系超低碳高强度低合金钢组织及低温韧性的影响.力学性能的测试结果表明,在终冷温度为450℃时,实验钢获得良好的强韧性配合,屈服强度为775MPa,韧脆转变温度为-55℃.组织观察及晶体学表征结果表明,随着终冷温度的降低,组织逐渐由粒状贝氏体向板条贝氏体和板条马氏体转变;终冷温度为450℃时,组织以板条贝氏体为主,多数的板条束包含三组不同的板条块,有效晶粒尺寸最小,大角晶界比例达到最大.解理裂纹扩展路径的观察结果表明,具有大角晶界的贝氏体板条块对解理裂纹扩展具有显著的阻碍作用,因此板条块尺寸细化、大角晶界比例增加是低温韧性改善的主要原因.
| [1] | Ghosh A, Das S, Chatterjee S, Rao Ramachandra P. Mater Charact, 2006; 56: 59
|
| [2] | Dong H. Sci China Technol Sci, 2012; 55: 1774
|
| [3] | Wang W, Shan Y Y, Yang K. Acta Metall Sin, 2007; 43: 578 (王 伟, 单以银, 杨 柯. 金属学报, 2007; 43: 578)
|
| [4] | You Y, Wang X M, Shang C J. Acta Metall Sin, 2012; 48: 1290 (由 洋, 王学敏, 尚成嘉. 金属学报, 2012; 48: 1290)
|
| [5] | Wang X Y, Pan T, Wang H, Su H, Li X Y, Cao X Z. Acta Metall Sin, 2012; 48: 401 (王小勇, 潘 涛, 王 华, 苏 航, 李向阳, 曹兴忠. 金属学报, 2012; 48: 401)
|
| [6] | Liu D S, Cheng B G, Luo M. Acta Metall Sin, 2011; 47: 1233 (刘东升, 程丙贵, 罗 咪. 金属学报, 2011; 47: 1233)
|
| [7] | Di G B, Liu Z Y, Hao L Q, Liu X H. Mater Mech Eng, 2008; 32(8): 1 (狄国标, 刘振宇, 郝利强, 刘相华. 机械工程材料, 2008; 32(8): 1)
|
| [8] | Zhou T, Yu H, Hu J, Wang S. Mater Sci Eng, 2014; A615: 436
|
| [9] | Xie Z, Fang Y, Han G, Guo H, Misra R D K, Shang C. Mater Sci Eng, 2014; A618: 112
|
| [10] | Wang C F, Wang M Q, Shi J, Hui W J, Dong H. Scr Mater, 2008; 58: 492
|
| [11] | Schino D A, Guarnschelli C. Mater Lett, 2009; 63: 1968
|
| [12] | Chen J, Tang S, Liu Z Y, Wang G D. Mater Sci Eng, 2013; A559: 241
|
| [13] | Sung H K, Shin S Y, Hwang B, Lee C G, Lee S. Metall Mater Trans, 2013; 44A: 294
|
| [14] | Nie W J, Shang C J, You Y, Zhang X B, Sundaresa S. Acta Metall Sin, 2012; 48: 797 (聂文金, 尚成嘉, 由 洋, 张晓兵, Sundaresa S. 金属学报, 2012; 48: 797)
|
| [15] | Morito S, Tanaka H, Konishi R, Furuhara T, Maki T. Acta Mater, 2003; 51: 1789
|
| [16] | Davis C L, King J E. Metall Mater Trans, 1994; 25A: 563
|
| [17] | Tomita Y, Okabayashi K. Metall Trans, 1986; 17A: 1203
|
| [18] | Naylor J P. Metall Trans, 1979; 10A: 861
|
| [19] | Morito S, Huang X, Furuhara T, Maki T, Hansen N. Acta Mater, 2006; 54: 5323
|
| [20] | Furuhara T, Kawata H, Morito S, Maki T. Mater Sci Eng, 2006; A431: 228
|
| [21] | Kitahara H, Ueji R, Tsuji N, Minamino Y. Acta Mater, 2006; 54: 1279
|
| [22] | Kawata H, Sakamoto K, Moritani T, Morito S, Furuhara T, Maki T. Mater Sci Eng, 2006; A438: 140
|
| [23] | Han S Y, Shin S Y, Seo C H, Lee H, Bae J H, Kim K, Lee S, Kim N J. Metall Mater Trans, 2009; 40A: 1851
|
| [24] | Shin S, Hwang B, Lee S, Kim N J, Ahn S. Mater Sci Eng, 2007; A458: 281
|
| [25] | Pickering F B, Gladman T. ISI Spec Rep, 1961; 81: 10
|
Full-Text
|
|
Contact Us
[email protected] QQ:3279437679 
WhatsApp +8615387084133
|
|