Raw rubber Latex contents, from 0% to 30% were used to stabilize lateritic samples to provide an alternative to cement stabilization. These samples were submitted to physical tests (water resistance test, absorption test) and mechanical tests (dry compressive strength test). The results indicate that samples made of latex content less than 15% dissolve completely into water. So it was impossible to make sample with these contents. Samples with 15% of raw rubber content or more are steady after water resistance test. The absorption rate of these samples decreases as the latex content increases. It goes from 14.45% for the samples at 15% to 5.87% for those at 30%. Therefore, the compressive strength test indicates that the resistance increases from 0.37 MPa for samples without latex to 3.15 MPa for those at 30% of latex content. Also, the rheological study shows that the samples pass from a brittle behaviour to a plastic behaviour when the latex content increases. The behaviour of the sample according to these different tests shows that this material can be used in several activity areas, such as construction, road building and sports area.
References
[1]
Ouattara, A. (1986) Historique et bilan de l’action du LBTP dans la promotion et le développement du géobéton comme matériau de construction. Bulletin du LBTP, No. 3, 9-20.
[2]
Fourdrin, S. (2004) Optimisation du procédé de fabrication des non-tissés par voie chimique: caractérisation de la réticulation du liant et étude des mécanismes d’adhésion fibre /liant. Thèse de Doctorat, Université des sciences et technologies de Lille, France, 24-80.
Alujas, A., Fernández, R., Quintana, R., Scrivener, K.L. and Martirena, F. (2015) Pozzolanic Reactivity of Lowgrade Kaolinitic Clays: Influence of Calcination Temperature and Impact of Calcination Products on OPC Hydration. Applied Clay Science, 108, 94-101. https://doi.org/10.1016/j.clay.2015.01.028
[5]
Souri, A., Golestani-Fard, F., Naghizadeh, R. and Veiseh, S. (2015) An Investigation on Pozzolanic Activity of Iranian Kailins Obtained by Thermal Treatment. Applied Clay Science, 108, 34-39. https://doi.org/10.1016/j.clay.2014.11.001
[6]
IRC (2018) Conférence internationale sur le caoutchouc (International Rubber Conference) thème la “Contribution de l’industrie du caoutchouc naturel au développement socio-économique et à la préservation de l’environnement” Abidjan, du 22 au 26 Octobre 2018. http://www.commodafrica.com
[7]
Cabane, N. (2004) Sols traités à la chaux et aux liants hydrauliques: Contribution à l’identification et à l’analyse des éléments perturbateurs de la stabilisation. Thèse de Doctorat, Ecole Nationale Supérieure des Mines Saint-Etienne, France, 189 p.
[8]
Terre, C.R.A., Houben, H. and Boubekeur, S. (1998) Blocs de terre comprimée: normes. Guide CDE, série technologie n°11, CRATerre-EAG, Villefontaine/Bruxelles, France/Belgique, 142 p.
[9]
Jolissaint, O.S P. (2015) Conception de briquettes de façade flexibles pour les murs arrondis. Doctorat science de la terre, Option Géomatériaux Université Félix Houphouet-Boigny Cocody, Abidjan; Côte d’Ivoire, 129 p.
[10]
Amzina, S.D. (2010) Production de blocs de terre comprimée traitées avec substances naturelles et caractérisation des propriétés hydriques. Master 2, institut international d’ingénierie et de l’eau, Ouaga (Burkina Faso), 66 p.
[11]
Sorgho, B., Bressollier, P., Guel, B., Zerbo, L., Ouedraogo, R., Gomina, M. and Blanchart, P. (2016) Etude des propriétés mécaniques des Géomatériaux argileux associant la décoction de Parkia biglobosa (néré). Comptes rendus chimie, 19, 895-901. https://doi.org/10.1016/j.crci.2016.01.016
[12]
Talla, P.A. (2010) Etude des constructions en briques de terre stabilisée à l’aide d’extrait de Parkia Biglobossa. Master 2, institut international d’ingénierie et de l’eau, Ouaga (Burkina Faso), 13-48.
[13]
Kouakou, C.H. and Morel, J.C. (2009) Mechanical Performance of Nonindustrial Building Material Manufactured with Clay as Natural Binder. Applied Clay Science, 44, 27-34. https://doi.org/10.1016/j.clay.2008.12.019
[14]
Offo, O.Q.A. (2017) Stabilisation de la latérite avec du latex d’hévéa: Applications diverses. Master Sciences de la Terre option Géomatériaux, Université felix Houphouet Boigny, Abidjan, 50 p.