This study shows a silver electrodeposition model (EDM) on a graphite substrate. The electrolyte was a 0.01 M solution of pure silver and chromium nitrate using an electrolyzing cell. EDC with current density up to 20 mA/cm2 and 15 mV and pulse current were studied. Results revealed that silver deposited at a rate of 0.515 mg/cm2/min with 12 mA/cm2 that decreases to 0.21 and 0.16 mg/cm2·min with the decrease of current density to 6 and 5 mA/cm2 respectively. The model postulates that silver ions (a) were first hydrated before diffusing (b) from the solution bulk to the cathode vicinity, The next step (c) involved the chemical adsorption of these ions on certain accessible sites of the graphite substrate (anode), The discharged entities (d) adhere to the graphite surface by Van der Vales force. Silver ions are deposited because the discharge potential of silver is low (0.38 mV) as compared to other metal ions like chromium (0.82 mV). Pulse current controls silver deposition due to flexibility in controlling steps (a)-(c) of the deposition mechanisms. Parameters like current density, current on-time, current-off time, duty cycle (ratio of current on time and total pulse time) and pulse frequency influenced the shape and size of the deposits. Step (b) suggested that silver particles were deposited in a monolayer thickness. The silver layer turned multiple after fully satisfying the accessible sites with the monolayer. The activation energy ΔE value amounts to 86.32 kJ/mol/K. At high temperature and current density, homogeneous diffusion occurs.
References
[1]
Sun, W., Chen, G. and Zheng, L. (2008) Electroless Deposition of Silver Particles on Graphite Nanosheets. Scripta Materialia, 59, 1031-1034. https://doi.org/10.1016/j.scriptamat.2008.06.046
[2]
De Riccardis, M.F. and Carbone, D. (2006) Electrodeposition of Well Adherent Metallic Clusters on Carbon Substrates. Applied Surface Science, 252, 5403-5407. https://doi.org/10.1016/j.apsusc.2005.12.055
[3]
Yoshinaga, M., Takahashi, H., Yamamoto, K., Muramatsu, A. and Morikawa, T. (2007) Formation of Metallic Ni Nanoparticles on Titania Surfaces by Chemical Vapor Reductive Deposition Method. Journal of Colloid and Interface Science, 309, 149-154. https://doi.org/10.1016/j.jcis.2007.01.051
[4]
Luo, K., Shi, N.L., Cong, H.T. and Sun, C. (2006) Electrophoretic Deposition of Nickel, Iron and Aluminum Nanoparticles on Carbon Fibers. Journal of Solid State Electrochemistry, 10, 1003-1007. https://doi.org/10.1007/s10008-005-0044-4
[5]
Srikanth, C.K. and Jeevanandam, J. (2009) Electroless Deposition of Silver on Synthesized Calcite via Surface Modification. Applied Surface Science, 255, 7153-7157. https://doi.org/10.1016/j.apsusc.2009.03.049
[6]
Tang, S., Tang, Y., Gao, F., Liu, Z. and Meng, X. (2007) Ultrasonic Electro-Deposition of Silver Nanoparticles on Dielectric Silica Spheres. Nanotechnology, 18, Article ID: 295607. https://doi.org/10.1088/0957-4484/18/29/295607
[7]
Sondi, I, Goia, D.V. and Matijevć, E. (2003) Preparation of Highly Concentrated Stable Dispersions of Uniform Silver Nanoparticles. Journal of Colloid and Interface Science, 260, 75-81. https://doi.org/10.1016/S0021-9797(02)00205-9
[8]
Rabah, M.A. (2013) Preparation of Size Controlled Silver Nanoparticles from E-Waste by Electrokinetic and Chemical and Electrokinetic Processes. International J. Chemical Materials Science and Engineering, 7, 75-80.
[9]
Mandich, N.V. (2021) Chemistry & Theory of Chromium Deposition: Part I— Chemistry. Plating and Surface Finishing, 84, 108-115.
[10]
Wang, D., Song, C., Hu Z. and Zhou, X. (2005) Synthesis of Silver Nanoparticles with Flake-Like Shapes. Materials Letters, 59, 1760-1763. https://doi.org/10.1016/j.matlet.2005.01.061
[11]
Cuenya, B.R. (2010) Synthesis and Catalytic Properties of Metal Nanoparticles: Size, Shape, Support, Composition, and Oxidation State Effects. Thin Solid Films, 518, 3127-3150. https://doi.org/10.1016/j.tsf.2010.01.018
[12]
Orináková, R., Škantárová, L., Orinák, A., Kupková, D.J. and Andersson, J.T. (2013) Electrochemical Deposition of SERS Active Nanostructured Silver Films. International Journal of Electrochemical Science, 8, 80-99.
[13]
Samanta S., Agarwal Sh. KishoreNair K., Richard A, Harris A and Swart H. (2019) Biomolecular Assisted Synthesis and Mechanism of Silver and Gold Nanoparticles. Materials Research Express, 6, Article ID: 082009. https://doi.org/10.1088/2053-1591/ab296b
[14]
Bian, J.-C., Li, Z., Chen, Z.-D., He, H.Y., Zhang, X.-W., Li, X. and Han, G.-R. (2014) Electrodeposition of Silver Nanoparticle Arrays on ITO Coated Glass and Their Application as Reproducible Surface-Enhanced Raman Scattering Substrate. Applied Surface Science, 258, 1831-1835. https://doi.org/10.1016/j.apsusc.2011.10.055
[15]
Pilone, D. and Kelsall, G.H. (2006) Prediction and Measurement of Multi-Metal Electro Deposition Rates and Efficiencies in Aqueous Acidic Chloride Media. Electrochimica Acta, 5, 3802-3808. https://doi.org/10.1016/j.electacta.2005.10.045
[16]
Song, X., Gunawan, P., Jiang, R., Su, J.L.S., Wang, K. and Xu, R. (2011) Surface Activated Graphite Nanospheres for Fast Adsorption of Silver Ions from Aqueous Solutions. Journal of Hazardous Materials, 194, 162-168. https://doi.org/10.1016/j.jhazmat.2011.07.076
[17]
Sun, Y. and Xia, Y. (2002) Shape-Controlled Synthesis of Gold and Silver Nanoparticles. Science, 298, 2176-2179. https://doi.org/10.1126/science.1077229
[18]
Zhu, J., Liu, S., Palchik, O., Koltypin, Y. and Gedanken, A. (2000) Shape-Controlled Synthesis of Silver Nanoparticles by Pulse Sonoelectrochemical Methods. Langmuir, 16, 6396-6399. https://doi.org/10.1021/la991507u
[19]
Yin, D., Liu, Y., Chen, P., Meng, G., Huang, G., Cai, L. and Zhang, L. (2020) Controllable Synthesis of Silver Nanoparticles by the Pulsed Electrochemical Deposition in a Forced Circulation Reactor. International Journal of Electrochemical Science, 15, 3469-3478. https://doi.org/10.20964/2020.04.57
[20]
Feynman, R., Leighton, R.B. and Sands, M. (1964). 2. Basic Physics. In: The Feynman Lectures on Physics (Vol. 1), Addison-Wesley, Boston.