酸洗对基体表面粗糙度的影响
|
Abstract:
本文研究了在前处理酸洗液中加入粗化剂，钕铁硼基体表面获得良好粗糙度的前处理酸洗工艺。试验结果表明，合适的酸洗粗化剂浓度是钕铁硼基体获得良好粗糙度的关键。用有机晶体粉末作为粗化剂可以获得粗糙度良好的基体表面。同时还研究了酸洗浓度、酸洗温度以及酸洗时间对钕铁硼基体表面粗糙度的影响。
In this paper, the pretreatment pickling process of NdFeB substrate surface with good roughness was studied by adding roughening agent into the pretreatment pickling solution. The test results show that suitable concentration of pickling roughening agent is the key to obtain good roughness of NdFeB matrix. The matrix surface with good roughness can be obtained by using organic crystal powder as roughening agent. The effects of pickling concentration, pickling temperature and pick-ling time on surface roughness of NdFeB substrate were also studied.
| [1] | 宋振纶, 李卫. 钕铁硼永磁材料表面防护技术: 特点·应用·问题[J]. 磁性材料及器件, 2008(1): 1-6. |
| [2] | 严芬英, 赵春英, 张琳. 钕铁硼永磁材料表面防护技术的研究进展[J]. 电镀与精饰, 2012, 34(8): 22-28. |
| [3] | 邓志伟, 张友亮, 张守华. 钕铁硼产品研磨倒角工艺优化[J]. 当代化工研究, 2022(15): 180-182. |
| [4] | 张守华, 张友亮, 邓志伟. 镀液添加剂对镀层内应力影响的研究[J]. 化工管理, 2021(6): 85-86. |
| [5] | 张友亮, 李滨, 张蒙, 等. 钕铁硼永磁材料沙镍工艺研究[J]. 信息记录材料, 2021, 22(7): 23-25. |
| [6] | 孙臣, 张伟, 严川伟. 前处理对烧结钕铁硼化学镀镍结合力的影响[J]. 腐蚀科学与防护技术, 2009, 21(2): 212-214. |
| [7] | 杨恒修, 冒守栋, 宋振纶. 酸洗对钕铁硼磁体电镀镍层防护失效的影响[J]. 稀有金属材料与工程, 2011, 40(12): 24-26. |
| [8] | 黄刚. 国内为Nd-Fe-B永磁防锈处理技术新进展[J]. 材料保护, 1993, 26(2): 4-5. |