Abstract:
本文研究了氧气斜吹旋转转炉碲渣的浸出工艺；考察了浸出剂、浸出时间、浸出温度、液固体积质量比、浸出剂浓度、双氧水加入量对铜、硒、碲浸出率的影响。结果表明：在浸出温度80℃、浸出时间3 h，盐酸浓度4 mol/L，液固体积质量比为5:1，双氧水加入量为0.2 ml/g碲渣，铜、硒、碲浸出率均达90%以上。
In this paper, the leaching process of tellurium slag from rotary converter with oxygen bias blowing was studied. The effects of extractant, leaching time, leaching temperature, volume-to-mass ratio of liquid to solid, concentration of leaching agent and amount of hydrogen peroxide on the leaching rate of copper, selenium and tellurium were investigated. The results show that the leaching rate of copper, selenium and tellurium is more than 90% at 80？C, 3 h, 4 mol/L hydrochloric acid, 5:1 volume-to-mass ratio of liquid to solid, 0.2 ml/g tellurium residue of hydrogen peroxide.
| [1] | 郑春到, 张伟旗. 从高铜碲渣中提取碲的实验研究[J]. 金属世界, 2017(3): 65-68+72. |
| [2] | 杨兴文. 不同价态含碲物料的湿法回收[J]. 有色冶炼, 1997(6): 1-12. |
| [3] | 吴文花, 刘吉波, 苏正夫, 王志坚. 从碲渣水浸渣中回收碲的研究[J]. 有色冶金(有色冶炼), 2013(8): 36-38. |
| [4] | 谢明辉, 王兴明, 陈后兴, 等. 碲的资源、用途与提取分离技术研究现状[J]. 四川有色金属, 2005(1): 5-8. |
| [5] | 方锦, 王少龙, 付世继. 从碲渣中回收碲的工艺研究[J]. 材料研究与应用, 2009, 3(3): 204-206. |
| [6] | 包新军, 刘吉波, 苏正夫, 等. 提高铅碲渣中碲浸出率的试验研究[J]. 稀有金属与硬质合金, 2013, 41(2): 10-13. |
| [7] | 刘兴芝, 宋玉林, 武荣成, 等. 碲化铜法回收碲的物理化学原理[J]. 广东有色金属学报, 2002, 12(S1): 55-58. |
| [8] | Hoffmann, J.E. (1989) Recovering Selenium and Tellurium from Copper Refinery Slimes. The Journal of the Minerals Metals Material Socierty, 41, 33-38. https://doi.org/10.1007/BF03220269 |
| [9] | 张博亚, 王吉坤, 彭金辉. 铜阳极泥中碲的回收[J]. 有色冶金(有色冶炼), 2006(2): 33-34+54. |
| [10] | 王清宏, 陈平, 黄淑芳. 从低品位原料中提取碲的工艺[J]. 上海有色金属, 2008, 29(3): 123-1266. |
| [11] | 何从行. 碲渣综合回收工艺研究[J]. 综合利用与环保, 2001(1): 41-45. |
| [12] | 陈芳兰, 车文婷. 从铋碲矿中回收碲[J]. 稀有金属与硬质合金, 1995(6): 4-7. |
| [13] | 王英, 陈少纯, 顾衍, 等. 从铜阳极泥回收碲的工艺研究[J]. 材料研究与应用, 2009, 3(2): 131-133. |
| [14] | 祝志兵. 碲铜复杂原料中碲回收工艺研究[J]. 铜业工程, 2010(3): 49-51. |