Películas delgadas de α-MoO3 preparadas por atomización pirolítica

moo3 thin films have been deposited on clean glass slides using the spray pyrolysis technique. the samples were grown with different thicknesses by spraying on common glass substrates a solution of (ammoniummolybdatetetrahydrate) ((nh3)6mo7o244h2o). the samples were characterized by x-ray diffraction (xrd), infrared spectroscopy, scanning electron microscopy (sem) and electrically through electrical resistivity measurements as a function of temperature. it was found that samples present crystalline structure associated with the alpha phase of moo3grown with preferential direction of growth along the planes (0k0). as result of increasing the volume of precursor solution sample surface becomes porous. the change in electrical resistance of moo3 films by exposure to carbon monoxide (co) at room temperature, makes the films obtained by this technique could be promising in its use in gas sensing devices at room temperature.