Steel treatment with calcium-aluminate synthetic slag and addition of titanium oxide

The paper introduces the results of the experiments on synthetic slag desulphurization and deoxidizing using slag belonging to the ternary system CaO-Al2O3-TiO2. The experiments have been done in a 10 kg induction furnace. In order to obtain the reducing slag we used a mixture of lime, alumina and titanium oxide, representing 2 % of the charge weight. The experiments were done on mechanical mixtures produced according to various recipes; for each experiment, the slag was sampled in order to determine its chemical composition and the steel was also sampled, in order to determine its contents in sulphur and oxygen. The resulting data have been processed in EXCEL, which gave the correlation equations between the desulphurization and deoxidizing output and the chemical composition of the synthetic slag, respectively the ratio and sum of the oxides. En el trabajo se presentan los resultados del experimento que se refiere a la desulfuración y desoxidación de las escorias sintéticas con escorias del sistema ternario CaO-Al2O3-TiO2.. Los experimentos se hicieron en un horno con inducción de 10 kg de capacidad. Para formar las escorias reductoras se ha utilizado una mezcla compuesta de cal, alúmina y óxido de titanio en porcentaje de 2 % del peso de la carga de acero más escoria sintética. Para los experimentos se usaron mezclas mecánicas producidas por varias recetas y de cada experimento se tomaron muestras de escorias para determinar la composición química y muestras de acero para determinar el contenido de azúfre y oxígeno. Los datos obtenidos fueron procesados en el programa de cálculo EXCEL, obteniéndose ecuaciones de correlación entre la eficiencia de la desulfuración y desoxidación y la composición química de la escoria sintética.